NOVEL HYDROPHILIC RESIN APPLIED IN HEAT-RESISTANT WATER-BORNE COATINGS
Z. Y. LIU
J. Y. WANG
Q. L. YAN
X. G. JIAN
Poly(phthalazinone ether nitrile ketone)s (PPENK) was modified with NaOH in N,N-dimethyl acetamide (DMAc) in order to find a hydrophilic resin applied in heat-resistant water-borne coatings. The properties of hydrolyzates (HPPENK) in different hydrolysis time were characterized by FT-IR and 1H-NMR, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), contact angle (water) as well as solubility measurements. The results indicated that, along with the prolonged hydrolysis time, nitrile groups conversion ratio and glass transition temperature (Tg) of hydrolyzates increase, whereas weight loss ratio of HPPENK decreases. As expected, the hydrophilicity of HPPENK was improved greatly, e.g., when CN conversion ratio was 93.82%, the water contact angles were found to decrease from 75.3Â° of PPENK to 54.4Â° of HPPENK. HPPENKc dispersion has no separation more than 20 days in terms of shelf-life.
In order to set up a list of libraries that you have access to,
you must first login
or sign up.
Then set up a personal list of libraries from your profile page by
clicking on your user name at the top right of any screen.