HYPERBRANCHED ALIPHATIC POLYESTER MODIFIED ACTIVATED CARBON PARTICLES WITH HOMOGENIZED SURFACE GROUPS
The hyperbranched aliphatic polyester grafted activated carbon (HAPE-AC), was successfully prepared by the simple "one-pot" method. The surface functional groups of commercial activated carbon particles were homogenized to hydroxyl groups by being oxidized with nitric acid and then reduced with lithium tetrahydroaluminate (LiAlH4) at first. Secondly, the surface hydroxyl groups were used as the active sites for the solution polycondensation of the AB2 monomer, 2, 2-bis(hydroxymethyl)propionic acid (bis-MPA), with the catalysis of p-toluenesulfonic acid (p-TSA). The homogenization of the surface groups of the activated carbon particles and the graft polymerization of the hyperbranched aliphatic polyester were investigated by X-ray photoelectron spectroscopy (XPS) technique. The products were also characterized with Fourier transform infrared (FT-IR) and scanning electron microscope (SEM). The competitive adsorption properties of the products toward the heavy metal ions (Cu(II), Hg(II), Zn(II), and Cd(II)) also proved the translations of the surface groups.
In order to set up a list of libraries that you have access to,
you must first login
or sign up.
Then set up a personal list of libraries from your profile page by
clicking on your user name at the top right of any screen.